Easy Construction Laying Textured and anti-slip Geomembrane 1.0mm-2.5mm for Slop application
Product Introduction
Jianyi HDPE textured geomembranes are available with either single- or double-sided textured surface which exhibit superior shear strength and the high multi-axial performance. The textured surface processing is the only one that produces a textured material without significant reduction of any physical properties. The product allows project for greater slopes to be designed since frictional characteristics are enhanced. Compared with smooth HDPE geomembranes, they have better friction features.
Geomembrane Series
Textured HDPE Geomembrane For Landfill project national standard (GB/T 17643-2011(GH-2T1,GH-2T2))
|
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
(CJ(City construction standard)-T234-2006)
| Specification | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark | |
| Item | ||||||||
| Thickness (mm) | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | ||
| Textured Highth (mm) | 0.25 | |||||||
| Density (g/c㎡,≥) | 0.94 | |||||||
| Tensile Properties | ||||||||
| Yield Strength (N/mm,LD/TD) | 15 | 18 | 22 | 29 | 37 | 44 | ||
| Breaking Strength (N/mm,LD/TD) | 10 | 13 | 16 | 21 | 26 | 32 | ||
| Yeild Elongation Rate (%) | 12 | |||||||
| Breaking Elongation Rate (%) | 100 | |||||||
| Rectangular Tear Strength (N) | 125 | 156 | 187 | 249 | 311 | 374 | ||
| Puncture Strength (N) | 267 | 333 | 400 | 534 | 667 | 800 | ||
| Environmental Stress Crack Resistance (h) (A single point of incision constant tensile method) |
300 | |||||||
| Carbon Black | ||||||||
| Carbon Black Content(Rang) (%) | 2.0~3.0 | |||||||
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 | |||||||
| Oxidative Induction Time (OIT) | ||||||||
| Standard OIT (min) | 100 | |||||||
| High Pressure OIT (min) | 400 | |||||||
| 85℃ Oven Ageing (Minimum Average) | ||||||||
| 90 days after baking, the standard OIT retention(%) | 55 | |||||||
| 90 days after baking, the hight pressure OIT retention(%) | 80 | |||||||
| The Anti-UV Strength | ||||||||
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) | 50 | |||||||
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) | 50 | |||||||
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | |||||||
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | |||||||
| Dimensional Stability | ±2 | |||||||
Forms Ordinary sheet size/roll:
| Thickness mm | Width meters | Length meters |
| 1.0 | 5.8/6 | 50 |
| 7 | 50 | |
| 1.5 | 5.8/6 | 50/100 |
| 7 | 50 | |
| 2.0 | 5.8/6 | 50 |
| 7 | 50 | |
| 8 | 50/100 |
HDPE Gemenbrane Texture Application
HDPE Geomembrane textured is used in applications that require increased frictional resistance, excellent chemical resistance and endurance properties.
HDPE Texture geomembrane spraying production equipment
Service
1, Free sample available
2, Trial order acceptable
3, Customized packing acceptable
4, Excellent after-sales service system
Changsha Jianyi New Material Co., Ltd., headquarter in Hunan and having branches in Surrounding cities , is one of the leading and comprehensive geosynthetics manufacture and installation service provider in China. Our HDPE geomembrane production capability is top ranking in recent years around our country. Our company have CE certificate for HDPE geomembrane series products as well as ISO9001, ISO14001 company certificates.
We have improved our textured geomembrane equipment last year by bringing new spraying processing system.